ʻAlumina Ceramic Filler High Alumina Inert Ball/99% alumina ceramic pōpō
Ke Kino A me Kemimiko o na Poepoe Seramika Inert
| Nā waiwai kino a me nā kemika o nā pōpō seramika inert | |||||||
| ʻElemu | Al2O3％ | 60 | 70 | 80 | 90 | 95 | 99 |
| Fe2O3％ | ≤0.9 | ≤0.8 | ≤0.6 | ≤0.4 | ≤0.3 | ≤0.1 | |
| Hiki ke hoʻoholo ʻia nā mea i koe ma o ke kūkākūkā ʻana ma waena o ka mea hoʻolako a me ka mea kūʻai aku inā pono. | |||||||
| hoʻomoʻa wai，％ | 3± 1, Hiki ke hoʻoholo ʻia ma ke kūkākūkā ʻana ma waena o ka mea hoʻolako a me ka mea kūʻai aku | ||||||
| ʻāpana, kg/m³ | 2.5-3.0 | 2.7-3.2 | 2.9-3.2 | ≥3.1 | ≥3.2 | ≥3.4 | |
| ʻAno nui，kg/m³ | 1400-1550 | 1400-1650 | 1500-1800 | 1700-1950 | 1800-1950 | ≥1900 | |
| Lehu, māwae a haki paha | ʻO ka ʻeke hoʻokahi ma lalo o 5% | ||||||
| ʻO ka hoʻokaʻawale ʻana | ʻAʻole ʻoi aku ka nui o ke anawaena o ka nui a me ka liʻiliʻi o ka pōʻai seramika ma mua o 1.2. | ||||||
| Ka hoʻomanawanui ʻana | ≤10mm | ±1.0 | |||||
| 11—25mm | ±1.5 | ||||||
| 26—50mm | ±2.0 | ||||||
| ≥50mm | ±3.0 | ||||||
| Ka ikaika hāʻule manuahi | Laki poho ≥99％ | ||||||
| Ka ikaika compressive | φ3 | ≥250 | ≥300 | ≥350 | ≥400 | ≥500 | ≥500 |
| φ6 | ≥800 | ≥1000 | ≥1000 | ≥1200 | ≥1500 | ≥1500 | |
| φ8 | ≥1500 | ≥1600 | ≥1800 | ≥2000 | ≥2500 | ≥2500 | |
| φ10 | ≥2000 | ≥2500 | ≥2800 | ≥3000 | ≥3500 | ≥3500 | |
| φ13 | ≥3000 | ≥3000 | ≥3500 | ≥4000 | ≥5000 | ≥5000 | |
| φ16 | ≥3500 | ≥4000 | ≥4500 | ≥5000 | ≥6000 | ≥7000 | |
| φ20 | ≥6000 | ≥6000 | ≥7000 | ≥8000 | ≥10000 | ≥12000 | |
| φ25 | ≥7000 | ≥7000 | ≥8000 | ≥10000 | ≥15000 | ≥17000 | |
| φ30 | ≥8000 | ≥9000 | ≥10000 | ≥12000 | ≥17000 | ≥19000 | |
| φ38 | ≥10000 | ≥12000 | ≥13000 | ≥15000 | ≥20000 | ≥22000 | |
| φ50 | ≥12000 | ≥14000 | ≥16000 | ≥18000 | ≥22000 | ≥26000 | |
| φ75 | ≥16000 | ≥18000 | ≥20000 | ≥22000 | ≥25000 | ≥30000 | |
| 50-75 | 55-75 | 60-80 | ≥80 | ≥82 | ≥85 | ||
| Ka helu ʻaʻahu % | ≤2 | ≤1 | |||||
| hikiwawe | ≤6 | ||||||
| alkalinity，％ | ≥77 | ≥85 | ≥90 | ≥92 | ≥95 | ≥97 | |
| ʻO ka refractoriness，℃ | ≥400 | ≥500 | ≥700 | ≥1000 | ≥1000 | ≥1000 | |
| Kū'ē i ka ʻokoʻa puʻe koke | Non-destructive rate ≥ 99%, ʻaʻohe hoʻololi i ka ikaika compressive a me ke kaomi ma hope o ka hoʻololi koke ʻana ma lalo o 25% | ||||||
| Kū'ē i ka hoʻololi koke o ka mahana | Laki poho≥99% | ||||||
| Pūʻolo | Puke pahu hao | Hoʻopili ʻia i loko o nā pahu hao, sila ʻia me nā ʻeke plastik mānoanoa PP a PE | |||||
| ʻeke ʻeke i ulana ʻia | Loaʻa i loko o nā ʻeke ulana paʻa a me ka pale UV | ||||||
| 'Ōlelo Aʻo: No ka ʻike wale nō ka ʻikepili ʻano nui, ʻaʻole i kumu no ka ʻae ʻana. | |||||||
'Ōlelo Aʻe: E nānā i ka Papa 5 No ka Hoʻomoʻa ʻana i ka wai o 99 mau pōpē hoʻopiha piha
| 99 Hoʻopiha wai kinipōpō piha | ||
| 99 mea hoʻopiha | anawaena | anawaena |
| ʻōwili ʻana | φ＜25mm | ＜5％ |
| Paʻi mīkini | φ＞25mm | ＜10％ |
99.5% Nā hōʻailona ʻenehana
| Al2O3 | ≥99% |
| SiO2 | ≤0.14% |
| Fe2O3 | ≤0.04% |
| CaO +MgO | ≤0.03% |
| TiO2 | ≤0.06% |
| Na2O | ≤0.1% |
| K2O | ≤0.1% |
Papa Kino o ka Poepoe Hoopiha Kemika
| KE KULANA | NUI |
| hoʻoluliluli hoʻouka (yb/t370-1995) | ʻO ka deformation ma lalo o 0.2mpa kaomi ma lalo o 0.6% |
| ʻO ke kūpaʻa haʻalulu wela (yb/t376.2-1995) | 1200°C a hiki i 600°C.10 mau manawa me ka ʻole o nā māwae |
| Hoʻololi hou i ka laina (gb/t3997.1-1998) | 1400 ℃ no 12 mau hola, ʻo ka helu kiʻekiʻe he 0.25%, ʻoi aku ka liʻiliʻi ma mua o 0.20% |
| ʻAno nui (gb/t2997-2000) | 3.2-3.50 g/cm3 |
| ikaika paʻi | E hui ma mua o 230 kg/cm2 |
| ʻIke ʻia ka porosity | 12-18% |
| ʻAno nui | 2.1-2.3g/cm3 |
Hoʻopaʻa Poepoe Kimia
1) Hoʻopili maʻamau: ʻeke ulana polyethylene me ke kaumaha ʻupena o 25kg, me ka pallet
2) Hoʻopili pahu kila: 100L pahu pahu kila, hiki ke hoʻohui ʻia nā pallets